MAKROPORE® 发泡母料


性能描述
Characteristics
特征
MAKROPOREsmasterbatches are designed for producing lightweight injection molded articles and /or for removing sink marks of injection molded products. MAKROPOREs secureextremely fine foam structure. Their active ingredient is an exothermic blowing agent based on azodikarbonamide.
MAKROPOREs发泡母料是为生产轻质注塑成型制品和/或无痕塑料制品设计的母料。MAKROPOREs提供非常细密的发泡结构,其活性成分是基于偶氮二甲酰胺的放热发泡剂。
Grades
级别
Makropore NAD 03 – contains bubble nucleating agent
Makropore NAD 03——含有发泡成核剂
Application
应用
Active components of THERMOBREAKpolymer consist of additives and stabilizer systems providing high resistance towards long-term heat exposure and ability to prevent the formation of burnt-in deposits in the ‘dead’ spaces of an extruder. The carrier matrix is polypropylene or low-density polyethylene.
THERMOBREAK母料的活性成分包括长效耐热的添加剂和稳定剂,能防止挤出机停机过程中形成煅烧沉积物。载体基质采用聚丙烯或低密度聚乙烯。
Handling
操作
There is no special limitation when handling these products; only generally valid hygienic rules should be observed.
操作无特殊限制,只需遵循常规的卫生规范。
Storage
储存
MAKROPOREs should be stored in a dry, cool and sheltered storage place.
MAKROPOREs发泡母料应存储在干燥、阴凉和有遮盖物的场所内。
Health Safety
健康安全
MAKROPORE is not designed for use in articles, which may come into contact with foodstuffs.
MAKROPORE不允许用于与食品接触的制品中。
General Information
基本信息

*decomposition of active ingredients starts at 165°C; the maximum is at 195°C
*recommended letdown ratio is 1–2% wt.
*masterbatches are simply mixed with basic material and dosed into the processing *equipment in an usual way
*screw revolution should be maintained at min. 75 min–1 to obtain very fine bubble structure
*温度达到165°C活性成分开始分解,温度195°C时达到最大值
*建议添加量为1–2% wt.。
*MAKROPORE发泡母料与原料简单混合后按照常规投料方式投料。
*螺杆转速应保持在最低75转/分钟,制品可获得非常精细的发泡结构。